The Determination of AMg6 alloy superplastic characteristics based on the free bulging test
P. 507–512.
The main aim of the present work is to get the first approximation of AMg6 alloy superplastic characteristics. In this study, constant pressure free bulging for superplastic material is analized by some simple analytical methods to determine the constants of the superplastic AMg6 alloy.
In book
Т. 2. , М.: МИЭМ НИУ ВШЭ, 2013.
Mikolaenko V., Анохин В. В., Кудряшов М. Д., В кн.: Межвузовская научно-техническая конференция студентов, аспирантов и молодых специалистов имени Е.В. Арменского. Материалы конференции.: М.: МИЭМ НИУ ВШЭ, 2022.
Сверхпластическая газовая формовка – это один из способов обработки материалов давлением, используемый при производстве тонкостенных изделий сложной геометрической формы. Для проектирования технологических режимов производства таких изделий используется компьютерное моделирование технологического процесса, для которого необходимо задать свойства материала. Основной экспериментальный метод исследования свойств сверхпластичных материалов – одноосное растяжение плоских образцов с постоянной скоростью деформации. Однако, стандартная ...
Added: December 12, 2024
Mikolaenko V., В кн.: Межвузовская научно-техническая конференция студентов, аспирантов и молодых специалистов им. Е.В. Арменского 2023.: МИЭМ НИУ ВШЭ, 2023.
Листовые заготовки из сверхпластичных материалов используются в технологиях сверхпластической газовой формовки для производства тонкостенных изделий сложной геометрической формы. При реализации такой технологии необходимо корректно задать режим давления и температуры, чтобы заготовка вошла в состояние сверхпластичности, при котором возможно её бездефектное формоизменение при больших деформациях. Режим давления и температуры устанавливаются исходя из модели деформационного поведения материала, ...
Added: April 2, 2024
Mikolaenko V., В кн.: Материалы конференции. Межвузовская научно-техническая конференция студентов, аспирантов и молодых специалистов им. Е.В. Арменского.: М.: МИЭМ НИУ ВШЭ, 2020. С. 16–18.
Работа посвящена компьютерному моделированию пластического формоизменения материала в условиях, близких к плоско-деформированному состоянию. Для моделирования такой задачи предлагается использовать метод конечных элементов с геометрическими ограничениями на элементы, что позволит учесть уширение образца, не прибегая к увеличению числа элементов при переходе от плоского моделирования к трехмерному. В рамках данной работы такой подход реализован в программных компонентах, ...
Added: January 31, 2023
Mikolaenko V., В кн.: Межвузовская научно-техническая конференция студентов, аспирантов и молодых специалистов имени Е.В. Арменского. Материалы конференции.: М.: МИЭМ НИУ ВШЭ, 2021. С. 39–42.
Применение эффекта сверхпластичности при реализации процессов обработки материалов давлением позволяет осуществлять бездефектное формоизменение листовых заготовок для получения оболочечных деталей сложной геометрической формы. Данный эффект возникает в специальных и промышленных сплавах на основе титана и алюминия. При разработке новых сплавов, обладающих эффектом сверхпластичности, особое внимание уделяется их деформационному поведению при повышенных температурах. Модель, описывающая деформационное поведение ...
Added: January 31, 2023
Mikolaenko V., В кн.: Межвузовская научно-техническая конференция студентов, аспирантов и молодых специалистов имени Е.В. Арменского. Материалы конференции.: М.: МИЭМ НИУ ВШЭ, 2022. С. 34–37.
Формовка листовых заготовок из сверхпластиче-ского материала - это технологический процесс, позволяющий получать тонкостенные изделия сложной геометрической формы. При реализации такого процесса необходимо задавать режим давления и температуры исходя из модели деформационного поведения материала. Существует множество экспериментальных методик, позволяющих получить такую модель, среди которых основной является механическое испытание плоских образцов на одноосное растяжение с постоянной скоростью ...
Added: January 31, 2023
Zakhariev I., Journal of Physics: Conference Series 2021 Vol. 1740 P. 1–6
Superplastic blow forming is a technology of shell parts production. The development of these processes requires computer simulation which cannot be realized without accurate parameters of the applied material. This characterization can be based on results of free bulging tests. Characterization techniques utilize the models of the dome growth during the bulging test. This study ...
Added: January 27, 2021
Odland J. Ø., International Journal of Environmental Research and Public Health 2020 Vol. 17 No. 5 P. 1724
Aluminium (Al) is a non-essential neurotoxicant and there is limited information regarding exposure to Al in utero. This study sought to evaluate the in utero exposure to Al in urban South African women, its effects on birth outcomes and possible synergistic effects between Al, essential and neurotoxic elements such as lead (Pb), mercury (Hg) and ...
Added: October 14, 2020
Mosleh A., Mikhaylovskaya A., Kotov A. et al., Metals 2017 Vol. 7 No. 12 P. 1–15
The paper focuses on developing constitutive models for superplastic deformation behaviour of near-αtitanium alloy (Ti-2.5Al-1.8Mn) at elevated temperatures in a range from 840 to 890 °C and in a strain rate range from 2 × 10−4 to 8 × 10−4 s−1. Stress–strain experimental tensile tests data were used to develop the mathematical models. Both, hyperbolic sine Arrhenius-type ...
Added: February 1, 2018
Mikhaylovskaya A. V., Mosleh A. O., Kotov A. et al., Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing 2017 No. 708 P. 469–477
Superplastic deformation behaviour of conventional sheets of a near-α titanium alloy (Ti-2.5Al-1.8Mn) was studied by a step-by-step decrease of the strain rate and constant strain rate tests in a temperature range of 790–915 °C. The research found that superplastic deformation is possible in a temperature range of 815–890 °С and a constant strain rate range ...
Added: December 1, 2017
Zakhariev I., Aksenov S. A., Journal of Chemical Technology and Metallurgy 2017 Vol. 52 No. 5 P. 1002–1007
Free bulging process is an experimental technique which can be used to characterize a sheet material in conditions of biaxial tension during hot forming. Analytical and semi-analytical models of this process are usually based on the hypothesis offering certain relations between the geometrical characteristics of a bulge during forming. The paper presents an original relation ...
Added: December 11, 2016
Kishchik M. S., Mikhailovskaya A. V., Levchenko V. S. et al., Metal Science and Heat Treatment 2017 Vol. 58 No. 9 P. 543–547
A proсеss for fabriсating 5.mm-thiсk shеets from alloy l565сh with rеcrystallized grains lеss than l0 µm in sizе is dеvеlopеd, whiсh involvеs supеrplastiс forming and providеs еlеvatеd mесhaniсal propеrtiеs at room tеmpеratuге.Тhе paramеtеrs of supеrplastiсitу and thе mесhaniсal propеrtiеs of alloy l565сh arе dеtегminеd. Tеst forming оf a domе-shapе modеl part is pеrformеd. ...
Added: October 19, 2016
Kotov A. D., Mikhaylovskaya A. V., Kishchik M. S. et al., Journal of Alloys and Compounds 2016 Vol. 688 P. 336–344
Highlights
•
Superplastic behaviour and the microstructural evolution were investigated.
•
Alloy with Al3(Sc,Zr) particles and alloy containing Al3Zr and Al3Ni particles.
•
Alloy with Ni and Zr exhibits a 1.5–2 times finer grains during deformation.
•
Al3Ni particles provide a larger number of nuclei for recrystallization.
Abstract
The superplastic properties of two high strength aluminium alloys are investigated. The first alloy contains fine, coherent ...
Added: September 9, 2016
Aksenov S. A., Zakhariev I., Osipov S. et al., Materials Science Forum 2016 Vol. 838-839 P. 552–556
Determination of material constants describing its behavior during superplastic gas
forming is the main subject of this study. The main feature of free bulging tests is the stress-strain
conditions which are very similar to ones occurring in the most of gas forming processes. On the
other hand, the interpretation of the results of such tests is a complicated ...
Added: November 23, 2015
Zakhariev I., В кн.: Авиакосмические технологии (АКТ-2015):Тезисы I тура XVI Всероссийской научно-технической конференции и школы молодых ученых, аспирантов и студентов.: Воронеж: ООО Фирма "Элист", 2015. С. 105–107.
The work is devoted to the definition OT4-1 alloy properties on the multidome forming experiments. For verification of obtained results computer simulation was performed. ...
Added: October 20, 2015
Chumachenko E., Portnoi V. K., Logashina I. V., Metallurgist 2015 Vol. 59 P. 69–75
Different test methods are described to determine the mechanical properties of materials in the superplastic state. The flow stress depends on strain and strain rate, the structural parameter of the materials, and temperature. The rheology and mechanics of superplastic deformation are discussed. The methods have been checked for reliability and produced good results in testing ...
Added: September 7, 2015
Zakhariev I., В кн.: Научно-техническая конференция студентов, аспирантов и молодых специалистов НИУ ВШЭ им. Е.В. Арменского. Материалы конференции.: М.: МИЭМ НИУ ВШЭ, 2015. С. 20–21.
Работа посвящена исследованию зависимости толщины, свободно формуемого купола в его вершине, от его высоты. Представлено описание имеющихся в литературе методов определения такой зависимости. С помощью метода конечных элементов произведена серия расчетов, процесса свободной газовой формовки куполов. Анализ полученных результатов позволил предложить аналитическое соотношение, описывающее зависимость толщины купола от его высоты. ...
Added: February 16, 2015
Puzino Y. A., Aksenov S. A., В кн.: Материалы VIII Всероссийской конференции по механике деформируемого твердого тела (Чебоксары, 16-21 июня 2014 г.): в 2 ч.Ч. 2.: Чебоксары: ФГБОУ ВПО "Чувашский государственный педагогический университет им. И.Я. Яковлева", 2014. С. 138–140.
A series of calculations of the stretching process with axisymmetric samples with different height in superplastic conditions using imitation simulation was held. As material was chosen Ti-Al6-V4 alloy. Dependencies of the obtained stresses and forces in central areas of samples from the size of the cylinders were obtained. ...
Added: January 19, 2015
Aksenov S. A., Chumachenko E., Osipov S. et al., Procedia Engineering 2014 Vol. 81 P. 1017–1022
This study proposes a method for determining the material constitutive equations and optimal forming conditions on the basis of free bulging tests. The blow-forming tests were carried out at the temperature of 420 °C using aluminum alloy (AMg-6) sheets of a 1 mm thickness. Each test was performed at constant pressure. For each fixed value ...
Added: October 16, 2014
Puzino Y. A., , in: Innovative Information Technologies: Materials of the International scientific–practical conference. Part 2* 2.: M.: HSE, 2014. P. 432–437.
This aim of this paper is the interpretation of the results of mechanical testing of materials to determine their properties under hot deformation. As an example, a simulation of rod stretching in superplasticity mode was considered. Comparing obtained data with the analytical solution was conducted. ...
Added: May 26, 2014
Chumachenko E., Смирнов О. М., Цепин М. А., М.: Либроком, 2009.
В монографии анализируются особенности технологических процессов деформирования материалов в условиях сверхпластичности и проблемы, возникающие при работе с материалами, обладающими повышенной скоростной чувствительностью. Приведена математическая постановка задачи о медленном течении физически нелинейных сред с учетом контактного трения, обсуждаются ограничения на применение модели и некоторые частные решения. Особое внимание уделено моделированию контактного взаимодействия в процессах обработки металлов ...
Added: January 17, 2014
Zakhariev I., В кн.: 12-я Международная конференция «Авиация и космонавтика – 2013». Тезисы докладов.: СПб.: Мастерская печати, 2013. С. 192–194.
В работе получено первое приближение механических свойств сплава АМг6 на основе результатов испытаний по свободной формовки куполов с постоянным давлением. Проведенный анализ позволил построить предварительную модель механических свойств сплава АМг6. ...
Added: December 24, 2013